Dear all,
There was no error when I performed gw calculation, but I wondered why the corrected energy band would appear in a relatively "chaotic" state. What are the reasons for this?
I have attach the relevant results below. Figure 1/2 shows the band structure calculated with/without GW correction respectively.
Thanks in advance.
Best,
Liu
GW QPband
Moderators: Davide Sangalli, andrea.ferretti, myrta gruning, andrea marini, Daniele Varsano
- claudio
- Posts: 464
- Joined: Tue Mar 31, 2009 11:33 pm
- Location: Marseille
- Contact:
Re: GW QPband
Dear Liu
probably it is not an error of the GW calculations but a problem in the interpolation.
When two bands cross each other in the GW, the interpolation could fail, because it is not able
to recognize the crossing.
My advice is to plot directly the points that you obtain from the GW without interpolation,
you should be able to recognize the bands and their path without strange behaviours.
best
Claudio
probably it is not an error of the GW calculations but a problem in the interpolation.
When two bands cross each other in the GW, the interpolation could fail, because it is not able
to recognize the crossing.
My advice is to plot directly the points that you obtain from the GW without interpolation,
you should be able to recognize the bands and their path without strange behaviours.
best
Claudio
Claudio Attaccalite
[CNRS/ Aix-Marseille Université/ CINaM laborarory / TSN department
Campus de Luminy – Case 913
13288 MARSEILLE Cedex 09
web site: http://www.attaccalite.com
[CNRS/ Aix-Marseille Université/ CINaM laborarory / TSN department
Campus de Luminy – Case 913
13288 MARSEILLE Cedex 09
web site: http://www.attaccalite.com
-
- Posts: 37
- Joined: Fri Nov 24, 2017 9:48 am
Re: GW QPband
Dear Claudio,
Thanks for your advise!
I'm not sure how to implement "plot directly without interpolation". I would appreciate it if you could explain it in detail. Thank you very much!
Best,
Liu
Thanks for your advise!
I'm not sure how to implement "plot directly without interpolation". I would appreciate it if you could explain it in detail. Thank you very much!
Best,
Liu
Dr. LIU Hongling
School of Physics, Shandong University
Jinan, CHINA
School of Physics, Shandong University
Jinan, CHINA
- Daniele Varsano
- Posts: 3936
- Joined: Tue Mar 17, 2009 2:23 pm
- Contact:
Re: GW QPband
Dear Liu,
you can plot the calculated QP energy that are found both in the o.qp* file and in the report file.
Best,
Daniele
you can plot the calculated QP energy that are found both in the o.qp* file and in the report file.
Best,
Daniele
Dr. Daniele Varsano
S3-CNR Institute of Nanoscience and MaX Center, Italy
MaX - Materials design at the Exascale
http://www.nano.cnr.it
http://www.max-centre.eu/
S3-CNR Institute of Nanoscience and MaX Center, Italy
MaX - Materials design at the Exascale
http://www.nano.cnr.it
http://www.max-centre.eu/